How Carbide Inserts Are Made

Manufacturing and machining shops that rely on carbide inserts for high speed tooling typically go through thousands of inserts each year. Machine operators work with many inserts each day, relying on their complex combination of chemistry and geometry to provide the cutting edges needed for precision, high speed production. Understanding how carbide tools are made and how the insert manufacturing processes influences their capabilities can help machine operators and manufacturers better understand their tools and overall processes.

What Carbide Inserts Are Made From

Most carbide inserts consist of cemented carbide, which is made from a combination of cobalt and tungsten carbide. Tungsten carbide’s hard particles within the insert provide the insert with its qualities of hardness, and cobalt acts as the binding agent, holding the materials solidly together. The size of the tungsten grains being used affects the insert’s hardness; larger grains (3-5 microns) result in softer, more quickly worn insert materials, while small grains (less than 1 micron) result in extremely hard, wear resistant inserts. The harder the tool, the more brittle it will be. When machining metals of exceptional hardness, harder inserts with smaller grains are typically used, while softer inserts are used most often in machining processes with interrupted cuts, which call for less brittle, tougher materials. The ratio of cobalt to tungsten carbide also influences carbide inserts’ hardness levels; cobalt is softer, so the more cobalt an insert contains, the softer it will be.

The Insert Manufacturing Process

After the engineer has determined what level of hardness needs to be achieved, the manufacturing process starts with powdered raw materials. Powdered tungsten, cobalt and carbon are milled and blended together with alcohol and water, creating a thick slurry. This substance is put into a dryer, which evaporates the liquids, leaving a thoroughly mixed powder. Carbide inserts then undergo a sintering process in which they are mixed with a polymer to form a paste, pressed into insert-shaped dies and placed in a high-heat furnace to be sintered. The polymer is melted out of the inserts during this step, and the inserts shrink.

Coating Carbide Inserts

For most machining applications, coated carbide inserts are used. Coatings provide added levels of hardness and wear resistance which become necessary, especially during high-speed machining or machining of extremely hard metals. Most carbide tools are coated using chemical vapor deposition, in which a metal is ionized with electrical currents and applied to the inserts in the form of vaporized condensation. Another common process is physical vapor deposition, which creates thinner coating layers resulting in sharper cutting edges ideal for machining hardened steel and titanium.